Ink Compatibility | Compatible with Original HP Latex Inks; also solvent, low-solvent, and UV-curable inks. |
Thickness (base vinyl) | 76 microns/3 mil per ISO 20534 Test Method |
Base Vinyl | Polymeric Calendered |
Liner | 160 g/m², double-sided PE-coated silicone paper with low-profile air release |
Adhesive | Gray, repositionable pressure-sensitive adhesive; 2 years removable with heat |
Opacity | 99% per TAPPI T-425 Test Method |
Finish | Gloss, >70 gloss units at 60˚ reflection |
Display Permanence (Outdoor unprinted) | Over 7 years, 2 years clean removable |
Display Permanence (Outdoor) | Over 4 years unlaminated, over 10 years laminated with HP 871 and 831 Latex Inks printed on the HP Latex 500 Printer series |
Display Permanence (Indoor home or office) | Over 7 years unlaminated, over 10 years laminated with HP 871 and 831 Latex Inks printed on the HP Latex 500 Printer series |
Display Permanence (Commercial in-window) | Over 5 years unlaminated, over 10 years laminated with HP 871 and 831 Latex Inks printed on the HP Latex 500 Printer series |
Indoor Floor Durability | Recommended on indoor smooth, non-porous, sealed flat and dry surfaces for up to 3 months |
Water Resistance | Water resistant with HP 871 and 831 Latex Inks printed on the HP Latex 500 Printer series |
Minimum Application Temperature | 15 to 26˚C (59 to 78˚F) on clean, dry surfaces |
Service Temperature | -40 to 65˚C (-40 to 149˚F) |
Operating Temperature | 15 to 35° C / 59 to 95° F |
Operating Humidity | 40 to 60% RH |
Lamination | Cold lamination; recommend using HP Gloss or Matte Polymeric Overlaminates |
Shelf Life | 2 years, unopened in original packaging |
Storage Temperature | 21 to 24° C / 69 to 75° F |
Storage Humidity | 50% RH |
Flame Resistance | B1 approved fire certification |
Environmental | REACH compliant |
Country of Origin | Product of United States |
Ordering Information | 4WM08A 1372 mm x 45,7 m (54 in x 150 ft) 4WM10A 1524 mm x 45,7 m (60 in x 150 ft) |
1. With HP 871 and 831 Latex Inks printed on the HP Latex 500 Printer series. Outdoor display permanence rating according to SAE J2527; in a vertical display orientation in simulated nominal outdoor display conditions for select high and low climates, including exposure to direct sunlight and water; performance may vary as environmental conditions change. For more information, see HPLFMedia.com/hp/printpermanence.
2. Recommended on indoor smooth, non-porous, sealed flat and dry surfaces for up to 3 months.
3. See the HP REACH Declaration published at HP Printing Products and Consumable Supplies.
4. B1 approved fire certification.
5. Outdoor unprinted display permanence rating based on white background color change according to SAE J2527; in a vertical display orientation in simulated nominal outdoor display
conditions for select high and low climates, including exposure to direct sunlight and water; performance may vary as environmental conditions change. For more information, see HPLFMedia.com/hp/printpermanence.
6. Outdoor display permanence rating according to SAE J2527; in a vertical display orientation in simulated nominal outdoor display conditions for select high and low climates, including
exposure to direct sunlight and water; performance may vary as environmental conditions change. For more information, see HPLFMedia.com/hp/printpermanence.
7. Display permanence rating for interior displays/away from direct sunlight by HP Image Permanence Lab and/or by Wilhelm Imaging Research, Inc. on a range of HP media. For more information, see HPLFMedia.com/hp/printpermanence.
8. Interior in-window display ratings by HP Image Permanence Lab on a range of HP media. HP predictions based on test data under Xenon-Arc illuminant—calculation assumes 6,000 Lux/12 hr day. For more information, see HPLFMedia.com/hp/printpermanence.
9. Performance varies based on printer and print profile. Water resistance testing by HP Image Permanence Lab on a range of HP media and follows ISO 18935 method. For more information, see: HPLFMedia.com/hp/printpermanence.
10. Based on internal HP testing exposure at -40°C (-40°F)/53% RH for 24 hours does not appear to have any effect on the peel strength from the substrate.